Vectran® is thermotropic and melts at 330°C. Key Features • High strength to weight ratio • Good creep resistance • High abrasion resistance • Excellent flex fatigue properties • Minimal moisture absorption • Excellent chemical resistance Disadvantages • Vectran® suffers from UV degradation, which causes strength loss and discoloration • Hair-like filaments tend to fray FIBER-LINE® PROCESS FOR VECTRAN® LIQUID CRYSTAL POLYMER • Coating • Twisting • Extrusion • Pultrusion • Precision Winding FIBER-LINE® VECTRAN® PRODUCTS • Strength Members • Ripcords • Belt & Hose Reinforcement Yarn • Industrial Fabric Yarn • Synthetic Wire Rope Abrasion  Yarn on Yarn Abrasion Ultraviolet (UV) Flame (Acid) (Alkali) (Organic Solvent) P P X P P P P Property UOM Value Breaking Tenacity g/d 23.0 Specific Gravity Ratio 1.40 Elongation @ Break % 3.8 Tensile Modulus g/d 600 Moisture Regain* %   LIQUID CRYSTAL POLYMER (LCP) LIQUID CRYSTAL POLYMER (HM) BARE FIBER PERFORMANCE * Equilibrium moisture regain @ 55% RH ** Creep @ 40%-58% ultimate tensile strength *** Shrinkage in dry air @ 177 C for 30 minutes  ABOUT FIBER-LINE® LOCATIONS Headquarters, R&D, Manufacturing FIBER-LINE® LLC 3050 Campus Drive Hatfield, PA 19440 +1 215.997.9181 fiber@fiber-line.com Manufacturing Operations FIBER-LINE® LLC 280 Performance Drive SE Hickory, NC 28602 +1 828.326.8700 fiber@fiber-line.com EMEA & Asia Pacific Operations FIBER-LINE® INTERNATIONAL B.V.

KEY PERFORMANCE PROPERTIES1 PHYSICAL NOMINAL VALUE UNIT TEST METHOD Density/Specific Gravity 1.00 ASTM D792 Melt Mass-Flow Rate (MFR) (230°C/2.16kg) 20 g/10 min ASTM D1238 MECHANICAL Tensile Strength 15.0 MPa ASTM D638 Flexural Modulus 1400 MPa ASTM D790 Flexural Strength 35.0 MPa ASTM D790 IMPACT Notched Izod Impact (Injection Molded) 150 J/m ASTM D256 ELECTRICAL Surface Resistivity < 100000 ohms/sq ASTM D257 PROCESSING INFORMATION INJECTION NOMINAL VALUE UNIT Drying Temperature 80 to 90 °C Drying Time 4.0 to 6.0 hr Processing (Melt) Temperature 220 to 250 °C Mold Temperature 30 to 80 °C Trilliant™ HC Electrically Conductive Formulations for Precision Performance Pipette Tips A critical design consideration for pipette tips is the accurate measurement of finite amounts of liquid.

TECHNICAL BULLETIN Characteristics Artisan™ Nylon Solution Painted Metal Painted Plastic Traditional Molded-in Color Impact Modified Nylon PA Ionomer Alloy Aesthetic Very Good Excellent Excellent Good Very Good Very Good Scratch Appearance Excellent Poor Poor Good Excellent Excellent Scratch & Mar Resistance Very Good Excellent Excellent Poor Very Good Excellent Color Customization Good Excellent Excellent Very Good Good Good Stress Whitening Excellent Fair Fair Poor Excellent Excellent Weatherability Good Excellent Excellent Very Good Good Very Good Temperature Performance Good Excellent Fair Fair Fair Good Corrosion Resistance Excellent Fair Excellent Excellent Excellent Excellent Processability One Step Multi Step Multi Step One Step One Step Complex One Step Total Production Cost $$$ $$$$$ $$$$ $$ $$$ $$$$ Order Quantity Restrictions Some Some Some None More More COMPARISON OF NYLON, METAL, AND PLASTIC Properties Test Method Artisan™ AR6000-0007 HI UV* Gloss Level** Gloss reading at 60 degrees 80-93 Molding Shrinkage – Across Flow ASTM D955 0.009 to 0.013 in/in Tensile Strength (Yield) ASTM D638 7300 psi Tensile Strength (Break) ASTM D638 5300 psi Tensile Elongation (Yield) ASTM D638 6.0% Flexural Modulus ASTM D790 270500 psi Flexural Strength (Yield) ASTM D790 9950 psi Notched Izod Impact ASTM D256 -4°F (-20°C) 5 ft-lb/in 73°F (23°C) 11 ft-lb/in Unnotched Izod Impact ASTM D256 -4°F (-20°C) 29 ft-lb/in 73°F (23°C) 30 ft-lb/in Color & Aesthetics*** Green, medium blue, dark blue, red, orange, white, gray, black Color customization available based on specific needs KEY PROPERTIES Features: high-gloss finish, UV stability, scratch resistance, chemical/corrosion resistance, cold temperature impact resistance, heat resistance * Reflects average of several colors, properties shift slightly depending on color ** Gloss level varies based on tooling temperature *** UV data available upon request Copyright © 2023, Avient Corporation.

OnColor™ UL 94 Colorants* • More than 2,000 recognized concentrates available worldwide in all color options • HB rating for most of PP, PS, ABS, PC/ABS, PBT, PA, PA-GF, TPU generic resins • V-0, V-1, V-2 and 5VA/5VB ratings for more than 200 specific engineering resins • Master file of recognized concentrates with scope of use accessible in the UL product finder • Development of custom products for specific resins upon request • Compliance Letters available for REACH and RoHS Cesa™ Flame Retardant Additives for Glow Wire • Fire performance in line with different levels of Glow Wire temperatures (IEC 60695-2-12) • Let-Down Ratio adjustable to reach different levels of Glow Wire temperatures • Non-halogen (in accordance with IEC 61249- 2-21) and non-HBCD** solutions • Wide range of solutions adapted to different polymers (PP, PS, PC) • Color and flame retardants can be combined in one product • Compliance Letters available for REACH and RoHS APPLICATION BULLETIN * Solutions also sold as Renol™ UL 94 Colorants APPLICATION POLYMER GWFI TEMPERATURE TYPICAL LET-DOWN RATIO CONTENT HIPS 750–960°C 5–10% Non-HBCD flame retardant** PC 850–960°C 2–4% Non-halogen in accordance with IEC 61249-2-21 PP homopolymer 850–960°C 4% Non-halogen in accordance with IEC 61249-2-21 PP copolymer 850–960°C 4–8% Antioxidant - metal deactivator ** Non-HBCD means that Hexabromocyclododecane (HBCD) is neither used as starting material during the mixing phase of our products nor intentionally added during production, but it cannot be excluded that it is not present at level of ubiquitous traces in any of the raw materials used in manufacturing of our products.

ONFLEX™ HT ONFLEX™ AF 7210 ONFLEX™ S KA ONFLEX™ S KG Applications Fasteners/ Defining Characteristic High temperature sealing Ambient temperature sealing High temperature sealing Ambient temperature sealing Density 1.00 g/ml 0.99 g/ml 1.10 g/ml 1.13 g/ml Physical Properties Tensile Strength 6.0–10.0 MPa 5.0–11.5 MPa 3.0–7.5 MPa 2.6–4.9 MPa Tear Resistance 25.0–37.0 kN/m 21.0–43.0 kN/m 17.0–46.0 kN/m 16.0–29.0 kN/m Compression Set 73°F (23°C) 72hrs 12–27% 16–32% 13–23% 31–35% 158°F (70°C) 22hrs 28–44% 32–43% 29–38% 62–66% 212°F (100°C) 22hrs 45–53% 56–60% 54–57% 80–85% Hardness 40–80 Shore A 40–80 Shore A 40–80 Shore A 40–80 Shore A Overmolding Substrate Polypropylene/ Polyethylene Polypropylene Polyamide Polyamide Processing Injection Molding/ HOW GLS TPEs MAKE THE DIFFERENCE IN AUTOMOTIVE FASTENERS AND CLIPS • Low compression set – coupled with good stress relaxation, our automotive TPEs are designed to maintain a good seal over time and reduce noise generated by vibration • High temperature performance – Avient automotive TPEs provide good sealing performance in temperatures up to 100°C/212°F • Bonding performance - strong chemical bond to polypropylene, polyethylene, and polyamide • Process flexibility - grades can be both injection molded and extruded • Easy to color - can be colored at the machine • Reduced production steps - some grades do not require pre-drying • Low VOC/FOG - OnFlex HT™ has been externally tested to VDA 278 and is proven to help satisfy vehicle interior air quality (VIAQ) regulatory requirements • Single source supply – we can streamline your supply chain with the ability to provide polymer colorants, engineered thermoplastics, and thermoplastic elastomers from a single source • Global support - we provide production, technical, and commercial support in locations convenient to your operations, including North America, Europe, and Asia To learn more about GLS TPEs for automotive applications, visit www.avient.com or call +1.844.4AVIENT (1.844.428.4368).

The coarse ground material was then crystallized in a vacuum oven at 160°C before drying the material at 160°C for approx. 4 hours within a PET drier • Plaques were then molded on a BOY XS and 10 of these were kept after each cycle, to take color measurements • This process was then repeated until 5 heat cycles had been completed RESULTS FOR RECYCLABILITY METHOD-1 As plaques were produced while the material went through five different melt heat histories, plaques were produced at each cycle and L*, a*, and b* values were measured. Key: A = 4% Amosorb SolO2-2 + Fortis Amber-1 @ 0.09%; B = 50% Regrind A + 50% Virgin PET; C = 50% Regrind A + 50% Virgin PET + Fortis Amber @ 0.045% REGRIND COMBINATION STUDY - METHODOLOGY 1.844.4AVIENT www.avient.com Copyright © 2022, Avient Corporation. It was also demonstrated that usage of a reduced amount of color, namely 0,045% of Fortis Amber-1, allows the production of bottles (Bottle C) that closely resembles the original bottles (Bottle A).

INDUSTRY BULLETIN STANDARD UNITS ONFLEX LO 7120-45N Volatile Organic Compounds VDA 278 ug/g(ppm) 41 Fogging VDA 278 ug/g(ppm) 521 Odor • Control • Dry conditions • Wet conditions SAE J1351 (15) 1-10 Scale 1 2 1 Compression Set (23°C) • 22 hours • 70 hours ASTM D395 % 14.4 14.6 Capillary Viscosity • 1341/s • 11170/s ASTM D3835 Pa*s 35 7 HVAC SYSTEMS OnFlex™ LO • Features: low VOC/FOG, low odor, good compression set, easy processing, overmolds to polypropylene • Example applications: seals and flaps in heating, ventilation and air conditioning systems CHARACTERISTICS ONFLEX™ LO ONFLEX™ AF TPE GENERAL PURPOSE TPV TPO Volatile Organic Compounds (VDA 278) Very Low Moderate Moderate Moderate Very Low Fogging (VDA 278 & DIN 75201) Very Low Moderate Moderate High Very Low Odor (VDA 270 Requirement ≤3.0) ≤3.0 ≤3.0 >3 >3 ≤3.0 Gloss Level Low Low Low Very Low High Tactile Feel Grippy Grippy Grippy Grippy Waxy Pre-Drying Required No No No Yes No Raw Material Costs $$ $$ $$ $$$ $ Compression Set @ RT Good Good Good Excellent N/A Compression Set @ ≥70°C Moderate Moderate Moderate Good N/A UV Resistance Good Excellent Good Good Good Weatherability Good Excellent Good Good Good Hardness Range Low to High Low to High Low to High Low to High High Density (g/ml) 1.15 0.99 0.90–1.20 0.95–0.98 0.90–1.20 GENERAL CHARACTERISTICS COMPARING TPE, TPV, TPO Grades shown on both pages are representative of solutions manufactured in North America, more grades available globally. INTERIORS/EXTERIORS TEMP STANDARD UNITS ONFLEX AF 7210-40B ONFLEX AF 7210-50B ONFLEX AF 7210-60B ONFLEX AF 7210-70B ONFLEX AF 7210-80B QUV Exposure • 1000 Hrs(0.68 W/m2 @ 340nm) • 2000 Hrs(0.68 W/m2 @ 340nm) 45°C ΔE 0.49 0.38 0.42 0.48 0.21 0.85 0.22 0.14 0.32 0.24 Xenon-Arc Exposure • 1000 Hrs(0.35 W/m2 @ 340nm) 63°C ΔE 0.63 0.84 0.34 — 0.58 Capillary Viscosity • 1341/s • 11170/s ASTM D3835 Pa*s 60 11.4 79 15 65 13 48 13.7 73 16 Ozone Resistance ASTM D1149(16) B Visual No cracks No cracks No cracks No cracks No cracks Low Temperature Brittleness ISO 812 B °C -63 -62 -62 -62 -62 OnFlex™ AF • Features: long-term sealing performance, reduced noise and vibration, grippy feel, low gloss, low odor, excellent UV resistance and weatherability, easy processability, overmolds to polypropylene • Example applications: trays, door pockets, fasteners, clips, roof rack pads, roof and door trim, and window encapsulations The need to innovate is virtually endless.

Many grades in the portfolio offer elevated Relative Thermal Index (RTI) ratings and Glow Wire Flammability Index (GWFI) up to 960°C. KEY CHARACTERISTICS • UL 94 V-2, V-0, 5VA ratings and elevated RTI ratings • GWFI (IEC 60695-11-10) up to 960°C • Comparative Tracking Index (CTI) PLC 0, 600V ratings • Injection molding and extrusion grades • Non-halogen grades available • Low dielectric performance with selected formulations • Good recyclability • Colorable MARKETS & APPLICATIONS Applications that require flame retardant performance including: • Transportation: Interior components, seat components, door panels, aircraft interiors, railway interiors, boat interiors • Construction & Building Materials: Cable insulation, pipes and fittings, insulation materials • Consumer – Appliance casings, housings, covers, fume hoods, battery packages, furniture • Industrial Equipment: Machine housings • Energy, Electrical & Electronic, E-Mobility: Battery frames, electrical housings, connectors • Telecommunication: Cable management • Packaging: Transportation of sensitive goods • Healthcare: Medical device housings and components PRODUCT BULLETIN MAXXAM FR FLAME RETARDANT POLYOLEFIN FORMULATIONS Non-halogenated Halogenated PP Homopolymer Copolymer Homopolymer Copolymer Unit Unfilled Glass Fiber Mineral Unfilled Glass Fiber Mineral Unfilled Glass Fiber Mineral Unfilled Glass Fiber Mineral Characteristic Talcum Talcum Talcum Talcum Reinforcement Mass-% 0 5–30 5–30 0 20–30 5-20 0 5–30 5–20 0 5–30 5–20 Colorable – ++ ++ + ++ ++ + + + + + + + Density g/cm3 0,9–1,08 1,28–1,37 0,98–1,55 0,92–1,06 1,25–1,35 0,95–1,28 0,94–1,04 1,3–1,55 1,01–1,42 0,96–1,01 0,94–1,58 0,95–1,46 Tensile Strength MPa 25–30 30–70 25–35 16–22 40–65 15–25 25-–35 30–70 25–35 20–24 20–55 -25 E-Modulus (Tensile) MPa 1600–2500 2500–8200 2500–4000 800–1200 2000–8000 1600–3000 1300–2000 3000–8900 1900–3500 1000–1400 1200–7500 1500–3000 Izod Impact 23°C notched % 2,0–4,5 3,5–7,5 2,5–4,5 5–40 2,5–18 2,5–6 2,5–4,5 3,5–6,0 3,0–7,0 4,0–40 2,5–16 2,5–10 Max. Temp (HDT 0,45 MPa) °C 60–100 80–145 80–160 40–80 60–120 60–110 60–100 80–145 80–145 40–80 60–120 60–110 Flammability, UL94 Step V2-V0/5VA V2-V0 V2-V0 V2-V0 V2-V0 V2-V0 V2-V0 V2-V0 V2-V0 V2-V0 V2-V0 V2-V0 Glow Wire Flammability Index °C 750–960 750–960 750–960 750–960 750–960 750–960 750–960 750–960 750–960 750–960 750–960 750–960 CTI V 450–00 450–600 450–600 450–600 450–600 450–600 350–600 350–600 350–600 350–600 350–600 350–600 Oil Resistance – + + + + + + + + + + + + Drying Required – Y Y Y Y Y Y Y Y Y Y Y Y Process (IM, EX, BM)1 – (IM, EX) (IM, EX) (IM, EX) (IM, EX) (IM, EX) (IM, EX) (IM, EX) (IM, EX) (IM, EX) (IM, EX) (IM, EX) (IM, EX) Other Modifications2 – Impact, HS, GB, T, HS, UV, LM GF, HS, UV, LM Impact, HS, GB, T, HS, UV, LM GF, HS, UV, LM Impact, HS, UV, LM GF, HS, UV, LM Impact, HS, GB, T, HS, UV, LM GF, HS, UV, LM Descriptions Lower density with moderate strength.

Wilflex Epic Rio RFU colors cure as low as 266°F (130°C), reducing energy consumption, dye migration, and the possibility of garment damage. Wilflex Epic Rio RFU Colors also provide exceptional wet-on-wet printing capabilities, an optimal soft hand, excellent stretch, and a matte finish.* HIGHLIGHTS • 33 most popular industry colors • Flexible cure profile (266°F/130°C to 320°F/160°C) • Excellent opacity • Wet-on-wet printing • Matte finish* • ECO PASSPORT by OEKO-TEX® and ZDHC MRSL Conformance Level 3 certifications** * Gloss may increase when cured at temperatures above 266°F (130°C) ** To learn about compliance standards applicable to specifics inks, please contact your Avient Specialty Inks distributor. For more information about Wilflex screen printing inks, please call 1.844.4AVIENT, email askspecialtyinks@avient.com or visit www.avientspecialtyinks.com or www.wilflex.com www.wilflex.com Yellow Swatch: Yellow: 1655 Swatch: 1655: 1795 Swatch: 1795: 2685 Swatch: 2685: 1235 Swatch: 1235: 116 Swatch: 116: Bright Red Swatch: Bright Red: 3546 Swatch: 3546: 7645 Swatch: 7645: 137 Swatch: 137: 1807 Swatch: 1807: 227 Swatch: 227: 1788 Swatch: 1788: 2397 Swatch: 2397: 2925 Swatch: 2925: 2768 Swatch: 2768: 805 Swatch: 805: 156 Swatch: 156: 3435 Swatch: 3435: 7488 Swatch: 7488: 287 Swatch: 287: 253 Swatch: 253: 296 Swatch: 296: 2145 Swatch: 2145: 806 Swatch: 806: 421 Swatch: 421: 348 Swatch: 348: 3005 Swatch: 3005: 809 Swatch: 809: 423 Swatch: 423: 2422 Swatch: 2422: 811 Swatch: 811: Black Diamond Swatch: PMS Black 3 C:

GLS TPE - Closurelogic Cap Liner - English CLOSURELOGIC GMBH A L U M I N U M C A P L I N E R • Compliance with food contact regulations • Seals to glass, PET and aluminum bottles • Excellent pressure retention for carbonated beverages • Provided a low migration TPE with outstanding organoleptic properties • Enabled processing at temperatures 20°C lower than comparative materials GLS™ Thermoplastic Elastomer KEY REQUIREMENTS WHY AVIENT?