Matrix Resin Fiber Reinforcement Fiber Content, by Weight (%) Epoxy E-CR or E-Glass >70% MATERIAL TECHNICAL DATA Property Test Procedure Rod Diameter 1.25 in (31.75 mm) 1.50 in (38.10 mm) Glass Transition Temp (Tg) ASTM 1356 100°C Minimum 100°C Minimum Water Absorption 24 hours at 50°C (122°F) ASTM D570 0.03% 0.03% Short Beam Strength (ILSS) ASTM 2344 8,400 psi (58 MPa) 9,200 psi (64 MPa) Transverse Shear Strength ASTM 7617 23,400 psi (160 MPa) 24,640 psi (170 MPa) Traceability Lot number shall be clearly marked on each package/shipment.

14 ksi, 96.5 MPa

MPA BLACK

MPA-CZ-01584 LIGHT GRAY

KEUNGGULAN KOMERSIAL Mengatur kegiatan kita di pasar tempat kita menghadirkan nilai kepada pelanggan. Nilai pribadi ini dimulai dari diri kita—penilaian dan keputusan yang kita buat sebagai individu memengaruhi cara pandang terhadap Avient di pasar dan di masyarakat tempat kita bekerja. Dalam melakukannya, kita akan mengumpulkan informasi teknis, biaya, produk, pasar, dan informasi lainnya tentang pasar dan pesaing kita secara sah dan etis melalui informasi yang tersedia secara publik, dan melalui pelanggan, analisis, penyelidikan, dan observasi.

PP OVERMOLDING HARDNESS REGULATORY STERILIZATION CHARACTERISTICS Dynaflex™ G2706 28A USP Class VI, ISO 10993, Food contact EtO Soft translucent grade, grippy feel Dynaflex™ G2711 43A USP Class VI, ISO 10993, Food contact EtO Highly colorable solution, grippy feel, low compression set Versaflex™ CL2242 & CL2250 42A/ 50A USP Class VI, ISO 10993, US Food contact EtO Clear boilable grades; ABS, PC bondable Versaflex™ G2705 N 60A USP Class VI, ISO 10993, Food contact EtO/Steam High resilience, low compression set Versaflex™ HC3810 20A-90A USP Class VI, ISO 10993 EtO General purpose, unfilled ABS, PC OVERMOLDING HARDNESS REGULATORY STERILIZATION CHARACTERISTICS Versaflex™ OM1040 40A USP Class VI, ISO 10993 EtO Translucent Versaflex™ OM3060 60A USP Class VI, ISO 10993 EtO Clear VERSAFLEX™ CL AND DYNAFLEX™ TPEs OVERMOLDING FOR ERGONOMICS • Adds good tactile surface with soft-touch feel • Available in a variety of color effects and textures • Improves grip, cushion, and comfort • Enhances functional performance like sealing properties, vibration damping, oxygen barrier, and scratch and abrasion resistance • Reduces assembly costs, good processability • Offers excellent adhesion to a wide range of substrates Applications: • Glucometers • Medical tools overmolds • Injector pens • Analysis devices VERSALLOY™ HC & VERSAFLEX™ HC TPEs SEALING & RESEALING • Rubbery feel and soft touch • No coring, good puncture, and resealability in static stoppers • Meets low coefficient of friction requirements in dynamic seals • Low extractables • Suitable to overmold onto polyolefins Applications: • Sealing and resealing septum • Seals and sanitary gaskets • Syringe plungers and tips MATERIAL DESCRIPTION HARDNESS REGULATORY STERILIZATION CHARACTERISTICS Versalloy™ HC 9210-45N 45A USP Class VI EtO Good processability, smooth surface aesthetics Versalloy™ HC 9210-55N 55A USP Class VI EtO Good processability, smooth surface aesthetics Versalloy™ HC 9210-70N 70A USP Class VI EtO Good processability, smooth surface aesthetics Versalloy™ HC 9220-43N 43A USP Class VI, ISO 10993-4/5 EtO Extrusion grade, high temperature resistance Versaflex™ HC 2110-35N 34A FDA, USP Class VI, ISO 10993 Autoclave EtO radiation Resealing, elevated comp set Versaflex™ HC 2110-57B 57A FDA, USP Class VI, ISO 10993 Autoclave EtO radiation Low stiction VERSAFLEX™ CL AND DYNAFLEX™ TPEs HIGH CLARITY GRADES WITHOUT PLASTICIZERS • Water clear grades formulated without phthalate plasticizers • Meets medical regulatory USP Class VI and ISO 10993-4,5 • Food contact and FDA compliant • Autoclave and radiation stable • Low extractable • High clarity (Haze 50 4.1, 100 4.5, 100 4, 70 6, 70 Tensile Modulus (MPa) 2200 2700 2600 2350 1820 1820 Flexural Strength (MPa) 80 90 104 86 68 68 Flexural Modulus (MPa) 2500 2700 2500 2300 1980 1590 HDT: 0.45, 1.8 (MPa) 110, 80 90, 80 100, 89 123, 100 123, 64 100, 70 UL-94 Rating @ 3.0 mm 5VA V-0 5VA V-0 HB V-0 UL-94 Rating @ 1.5 mm V-0 V-0 5VB V-0 HB V-0 UL-94 Rating @ 0.75 mm V-1 V-2 V-0 None None V-2 COMPETITIVE MATERIAL COMPARISON ENGINEERED POLYMER FORMULATIONS FOR HEALTHCARE TRILLIANT™ HC THERMOPLASTICS The family of Trilliant™ HC high-performance thermoplastics is formulated to meet the growing challenges of medical devices and equipment. MATERIAL DESCRIPTION BASE RESIN Trilliant™ HC2020 Copolyester Trilliant™ HC8910/8920 Polyketone/ABS blend Trilliant™ HC2120 Tritan Trilliant™ HC3120 PC Trilliant™ HC5210 PP Trilliant™ HC6010 PA6 Trilliant™ HC6610 PA66 Trilliant™ GRV-NP-110-W PA12 TRILLIANT™ HC THERMOPLASTICS • Chemically resistant replacement for FR PC/ABS, FR PC/PET & FR COPE, providing UL 94 Yellow Card V-0 flame rating at 1.5 mm, V-1 at 0.75 mm thicknesses for a broad color spectrum • Outperforms PC/ABS, PC/PET and COPE in resistance to common disinfectants • Retains tensile strength after 72-hour exposure to common hospital disinfectants, and shows better long-term chemical resistance as compared to PC blends and COPE • Exhibits good impact and temperature resistance • Available in natural grades, standard medical colors, or custom pre-colored products Applications: • Medical device housings • MRI, X-ray, CT scanner components • Surgical instruments such as staplers, dissectors, scissors • Auto-injector pen TRILLIANT™ HC ELECTRICALLY CONDUCTIVE FORMULATIONS • Consistent conductivity ensures repeatable part performance and minimizes failures related to inconsistent electrical conductivity • High flow and easy processing facilitate filling of thin wall parts and multiple cavity tools, which enable faster cycle times and lower per-unit part costs • Superior durability reduces breakage and resultant scrap related costs • Less tendency to flash results in improved appearance and less fluid retention in or on the tip, thus driving greater accuracy and less potential for cross-contamination • High strength produces parts with greater stiffness and warp resistance, again minimizing scrap-related costs Applications: • Conductive pipette tips TEST TEMS SPECIFIC GRAVITY MELT FLOW RATE (230OC, 2.16KG) TENSILE STRENGTH FLEXURAL STRENGTH FLEXURAL MODULUS IMPACT STRENGTH NOTCHED, IZOD SURFACE RESISTIVITY Method ASTM D-792 ASTM D-1238 ASTM D-638 ASTM D-790 ASTM D-790 ASTM D-256 ASTM D-257 Unit -- g/10min MPa MPa MPa J/m Ohms/sq.

PRODUCT MATERIAL DESCRIPTION COLOR MAX THICKNESS IN (MM) MAX WIDTH IN (CM) FLEXURAL MODULUS Msi (GPa) FLEXURAL STRENGTH ksi (MPa) GLASS % GC-70-UL Glass/Epoxy Any 0.1 (2.5) 17.75 (45) 5.8 (39.99) 210 (1448) 70 GC-66-ULW Glass/Epoxy, 90° Weft Any 0.1 (2.5) 17.75 (45) 4.5 (31.03) 130 (896) 66 GC-70-ULS Glass/Epoxy, 1080 Woven Scrim Any 0.1 (2.5) 17.75 (45) 5.8 (39.99) 210 (1448) 70 GC-70-ULZ Glass/Epoxy Natural 0.04 (1.0) 8.75 (22.2) 6.8 (46.89) 245 (1689) 70 GC-70-ULC Carbon/Epoxy Black 0.04 (1.0) 8.0 (20.3) 19.9 (137.21) 300 (2069) 70 http://www.avient.com/content/product-selection-help-form BARSTOCK All barstock composites are machined to size with a surface finish prepared to fit customer requirements. STANDARD BARSTOCK PRODUCTS PRODUCT MATERIAL DESCRIPTION COLOR MAX THICKNESS IN (MM) MAX WIDTH IN (CM) FLEXURAL MODULUS Msi (GPa) FLEXURAL STRENGTH ksi (MPa) GLASS % GC-67-UB Glass/Epoxy Black 0.575 (14.6) 11.75 (29.8) 5.8 (39.99) 153 (1055) 67 GC-67-UBZ Glass/Epoxy Black 0.5 (12.7) 8.75 (22.2) 5.8 (39.99) 153 (1055) 67 GC-60-UBC Carbon/Epoxy Black 0.25 (6.35) 4.0 (10.2) 12.5 (86.19) 150 (1034) 60 GC-67-UBW Glass/Epoxy, 90° Weft Blue 0.25 (6.35) 8.75 (22.2) 4.8 (33.10) 150 (1034) 67 http://www.avient.com/content/product-selection-help-form PULTRUDED PROFILES - TYPICAL PROPERTIES The Glasforms™ pultrusion process creates continuous, constant cross-sectional profiles with consistent, uniform quality and exceptional mechanical performance. TENSILE STRENGTH ksi (MPa) TENSILE MODULUS Msi (GPa) FLEXURAL STRENGTH ksi (MPa) FLEXURAL MODULUS Msi (GPa) COMPRESSIVE STRENGTH ksi (MPa) DENSITY lb/in3 (g/cm3) GLASS % ASTM Standard ASTM D3916/D638 ASTM D3916/D638 ASTM D4476/D790 ASTM D4476/D790 ASTM D695 ASTM D792 ASTM D2584 Glass Fiber Reinforced 110-150 (750-1000) 5.5-7.0 (38-48) 100-130 (700-900) 5.5-6.5 (38-45) 60-110 (415-750) .068-.073 (1.9-2.0) 65-75 Carbon Fiber Reinforced 405 (2800) 24 (165) 180 (1200) 21 (145) 150 (1000) 0.058 (1.6) 75 Multiaxial Glass Reinforced 45-60 (310-415) 2.6-3.5 (18-24) 65 (450) 2.1-2.7 (15-19) 40 (275) 0.066 (1.8) 45-55 STANDARD SIZES http://www.avient.com/content/product-selection-help-form CONTINUOUS FILAMENT WOUND PROFILES This table represents examples of common continuous filament wound profile sizes.

KEY PERFORMANCE PROPERTIES1 PHYSICAL NOMINAL VALUE UNIT TEST METHOD Density/Specific Gravity 1.00 ASTM D792 Melt Mass-Flow Rate (MFR) (230°C/2.16kg) 20 g/10 min ASTM D1238 MECHANICAL Tensile Strength 15.0 MPa ASTM D638 Flexural Modulus 1400 MPa ASTM D790 Flexural Strength 35.0 MPa ASTM D790 IMPACT Notched Izod Impact (Injection Molded) 150 J/m ASTM D256 ELECTRICAL Surface Resistivity < 100000 ohms/sq ASTM D257 PROCESSING INFORMATION INJECTION NOMINAL VALUE UNIT Drying Temperature 80 to 90 °C Drying Time 4.0 to 6.0 hr Processing (Melt) Temperature 220 to 250 °C Mold Temperature 30 to 80 °C Trilliant™ HC Electrically Conductive Formulations for Precision Performance Pipette Tips A critical design consideration for pipette tips is the accurate measurement of finite amounts of liquid.

G675/SC-10 Swellcoat® E-Glass 22.7 LBs (50 KG) 1835 Ft/LB (1233 M/KG) Flat TBD ??? PBO1500 FIBER-LINE® BondcoatTM Zylon 125 LBs (56 KGs) 8480 FT/LB (5696 M/KG) Flat .421 mm N/A Strength member treated with adhesion pro- moting coating. K58220T N/A Kevlar® 2480 LBs (1125 KGs) 230 FT/LB (154 M/KG) Flat 2.81 mm N/A Strength member in cable application Product ID FIBER-LINE® Polymer Jacket Base Fiber Break Strength Yield Geometry Nominal Diameter Description 13.75mm K/Hytrel Hytrel Jacket Kevlar® 29000 LBs (13154 KGs) 138 KGs/KM Round 13.75mm Kevlar rope w/ Hytrel extruded jacket 12.5mm K/TPU TPU jacket Kevlar® 24000 LBs (10885 KGs) 115 KGs/KM Round 12.5mm Kevlar rope w/ Hytrel extruded jacket 7.87mm K/MDPE MDPE Jacket Kevlar® 24000 LBs (10885 KGs) 50 KGs/KM Round 7.87mm Kevlar w/ MDPE extruded jacket .58mm C/PU TPU jacket Carbon 74 LBs (33.6 KGs) N/A Round/ Flat .58mm Carbon w/ TPU extruded jacket 4.50mm K/HDPE HDPE jacket Kevlar® 2000 LBs (907 KGs) 16 KGs/KM Round 4.06 mm Kevlar w/ HDPE extruded jacket POPULAR JACKETED STRENGTH MEMBERS MOVING HIGH PERFORMANCE FIBERS FORWARD This data is provided for informational purposes only, and does not constitute a specification.

Product ID FIBER-LINE® Coating Base Fiber Nominal Break Strength Nominal Yield Description G675/Colors FIBER-LINE® Colorcoat™ E-Glass 60 LBs (27 KGs) 1897 FT/LB (1274 M/KG) Color formula designed to be compatible with customer specific resin matrix K1420 FIBER-LINE® Flamecoat™ Kevlar® 65 LBs (29 KGs) 6872 FT/LB (4616 M/KG) Flame retardant coating suppresses flame and smoke K1500 FIBER-LINE® Protexcoat™ FIBER-LINE® Colorcoat™ Kevlar® 69 LBs (31 KGs) 8770 FT/LB (5892 M/KG) Kevlar® coated with UV inhibitors and carbon black pigment for UV protection K14200 FIBER-LINE® Repelcoat™ Kevlar® 650 LBs (294 KGs) 877 FT/LB (588 M/KG) Water repellant coating used in ballistic fabric applications V3000T N/A Vectran® 195 LBs (88 KGs) 4390 FT/LB (2950 M/KG) Twisted to improve processing POPULAR INDUSTRIAL FABRIC YARN PRODUCTS MOVING HIGH PERFORMANCE FIBERS FORWARD LOCATIONS Headquarters, R&D, Manufacturing FIBER-LINE® LLC 3050 Campus Drive Hatfield, PA 19440 +1 215.997.9181 fiber@fiber-line.com Manufacturing Operations FIBER-LINE® LLC 280 Performance Drive SE Hickory, NC 28602 +1 828.326.8700 fiber@fiber-line.com EMEA & Asia Pacific Operations FIBER-LINE® INTERNATIONAL B.V.