PET POLYESTER DATA PET POLYESTER BARE FIBER PERFORMANCE * Equilibrium moisture regain @ 55% RH ** Creep @ 40%-58% ultimate tensile strength *** Shrinkage in dry air @ 177 C for 30 minutes ABOUT FIBER-LINE® LOCATIONS Headquarters, R&D, Manufacturing FIBER-LINE® LLC 3050 Campus Drive Hatfield, PA 19440 +1 215.997.9181 fiber@fiber-line.com Manufacturing Operations FIBER-LINE® LLC 280 Performance Drive SE Hickory, NC 28602 +1 828.326.8700 fiber@fiber-line.com EMEA & Asia Pacific Operations FIBER-LINE® INTERNATIONAL B.V.

TECHNICAL BULLETIN 1.844.4AVIENT www.avient.com PROPERTY TEST METHOD UNITS VERSAFLEX™ CE 3130-80N VERSAFLEX™ CE 3130-70N Shore Hardness ASTM D2240 Shore A 79 69 Specific Gravity ASTM D792 g/cm3 1.08 1.04 Tensile Strength ASTM D412 psi 2,484 2,222 Melting Flow Index (190°C, 21.6kg) ASTM D1238 g/10min 5.2 4.4 Elongation ASTM D412 % 864 667 Flexural Modulus @ 300% ASTM D790 psi 975 855 Viscosity @ 11,170 sec, 200°C ASTM D3835 Pa.s 30.6 22.2 Abrasion (Mass Lost) ASTM D3389 mg 1.1 2.6 UV Resistance 0.68W/m2 45°C 168hours — Good Good Stain Resistance *Condition 1 *Condition 2 — Excellent Excellent Blooming 85% RH 30°C,168 hours — Non Non Processing (Demold) — — Excellent Good Cycle Time — — Short Middle Overmold Substrate — — PC/ABS PC/ABS KEY PROPERTIES AND OVERMOLD PERFORMANCE Copyright © 2021, Avient Corporation. TEST METHODS Stain Test - Condition 1: Tea, coffee, ketchup, mustard stand on the surface for 2 minutes at room temperature, then removed to observe the surface performance.

TEST METHOD Fifteen bars of each material were placed into jigs at 1% and 2% strain. This procedure was completed by placing one 1/2 inch section of rayon gauze at the apex of each bar, and soaking the gauze with the disinfectant to saturate the material.

LOCATIONS Headquarters, R&D, Manufacturing FIBER-LINE® LLC 3050 Campus Drive Hatfield, PA 19440 +1 215.997.9181 fiber@fiber-line.com Manufacturing Operations FIBER-LINE® LLC 280 Performance Drive SE Hickory, NC 28602 +1 828.326.8700 fiber@fiber-line.com EMEA & Asia Pacific Operations FIBER-LINE® INTERNATIONAL B.V.

LOCATIONS Headquarters, R&D, Manufacturing FIBER-LINE® LLC 3050 Campus Drive Hatfield, PA 19440 +1 215.997.9181 fiber@fiber-line.com Manufacturing Operations FIBER-LINE® LLC 280 Performance Drive SE Hickory, NC 28602 +1 828.326.8700 fiber@fiber-line.com EMEA & Asia Pacific Operations FIBER-LINE® INTERNATIONAL B.V.

POLYBENZYLOATE (PBO) DATA POLYBENZYLOATE (PBO) BARE FIBER PERFORMANCE * Equilibrium moisture regain @ 55% RH ** Creep @ 40%-58% ultimate tensile strength *** Shrinkage in dry air @ 177 C for 30 minutes  ABOUT FIBER-LINE® LOCATIONS Headquarters, R&D, Manufacturing FIBER-LINE® LLC 3050 Campus Drive Hatfield, PA 19440 +1 215.997.9181 fiber@fiber-line.com Manufacturing Operations FIBER-LINE® LLC 280 Performance Drive SE Hickory, NC 28602 +1 828.326.8700 fiber@fiber-line.com EMEA & Asia Pacific Operations FIBER-LINE® INTERNATIONAL B.V.

Main activity 31/08/201820084675101 Registered entity Legal Situation Normal situation 26/11/2021 4Extract from Page 4from Document issued in accordance with Article III.34, §1 of the Code of Economic Law The legal terms were translated literally. Main activity 31/08/201820084675101 Document issued in accordance with Article III.34, §1 of the Code of Economic Law The legal terms were translated literally.

This product selection guide provides detailed information to help you select the Maxxam product that’s right for your application. 4 Product Code - - - PP5113 B44 F5134T2-4 PP5130 B63 F5134T4-1 Filler Percentage - % - 13 20 30 40 Tensile Strength Yield psi ASTM D638 5000 4800 4600 4500 MPa ISO 527 33 33 32 31 Tensile Elongation Yield % ASTM D638 6 4 3 2 Break % ASTM D638 60 30 15 10 Flexural Modulus 73°F (23°C) psi ASTM D790 300,000 360,000 400,000 460,000 MPa ISO 178 2300 2450 2900 3300 Notched Izod 73°F (23°C) ft-lb/in ASTM D256 0.65 0.60 0.55 0.50 kJ/m2 ISO 180 3.50 3.3 3.00 2.75 Heat Deflection 66 psi °F ASTM D648 230 240 260 275 °C ISO 75 110 116 127 135 264 psi °F ASTM D648 130 140 150 175 °C ISO 75 54 60 66 79 Specific Gravity 73°F (23°C) - ASTM D792 0.99 1.04 1.15 1.25 Linear Shrinkage 1/8 in wall % - 1.2–1.6 1.0–1.4 0.8–1.2 0.6–1.0 3.2 mm wall % - 1.2–1.6 1.0–1.4 0.8–1.2 0.6–1.0 Product Code - - - PP6113 A77-SM PP6120 B16-2 PP6130 B11 PP6135 B40-UV Filler Percentage - % - 13 20 30 35 Tensile Strength Yield psi ASTM D638 4350 3500 2600 3700 MPa ISO 527 30 24 18 26 Tensile Elongation Yield % ASTM D638 5 4 7 6 Break % ASTM D638 35 70 150 70 Flexural Modulus 73°F (23°C) psi ASTM D790 290,000 280,000 280,000 390,000 MPa ISO 178 2000 1950 1750 2700 Notched Izod 73°F (23°C) ft-lb/in ASTM D256 0.7 2.7 4.5 0.65 kJ/m2 ISO 180 4.0 14 24 3.5 Heat Deflection 66 psi °F ASTM D648 239 215 225 250 °C ISO 75 115 102 107 123 264 psi °F ASTM D648 140 125 130 150 °C ISO 75 60 52 54 60 Specific Gravity 73°F (23°C) - ASTM D792 0.99 1.05 1.15 1.18 Linear Shrinkage 1/8 in wall % - 1.1–1.5 .9–1.3 0.7–1.1 0.5–0.9 3.2 mm wall % - 1.1–1.5 .9–1.3 0.7–1.1 0.5–0.9 Maxxam™ Talc-Filled Copolymer Polypropylene Maxxam™ Talc-Filled Homopolymer Polypropylene Offers a moderate level of impact strength and improved stiffness and heat deflection performance. Offers high levels of stiffness and heat deflection performance. 51.866.POLYONE www.polyone.com Product Code - - - PP5210 A111 PP5220F A1 PP5230F PP5240 A111 Filler Percentage - % - 10 20 30 40 Tensile Strength Yield psi ASTM D638 4600 4300 3900 3500 MPa ISO 527 32 30 27 24 Tensile Elongation Yield % ASTM D638 7.0 6.0 5.5 5.0 Break % ASTM D638 125 115 100 70 Flexural Modulus 73°F (23°C) psi ASTM D790 250,000 285,000 310,000 340,000 MPa ISO 180 1600 1900 2100 2300 Notched Izod 73°F (23°C) ft-lb/in ASTM D256 0.70 0.70 0.70 0.70 kJ/m2 ISO 180 3.85 3.85 3.85 3.85 Heat Deflection 66 psi °F ASTM D648 190 210 225 240 °C ISO 75 88 99 107 116 264 psi °F ASTM D648 120 125 130 133 °C ISO 75 49 52 54 56 Specific Gravity 73°F (23°C) - ASTM D792 0.96 1.04 1.15 1.25 Linear Shrinkage 1/8 in wall % - 1.3–1.7 1.1–1.5 0.9–1.3 0.7–1.1 3.2 mm wall % - 1.3–1.7 1.1–1.5 0.9–1.3 0.7–1.1 Product Code - - - PP6210 A11 PP7220 A614 PP6230F A1 PP6240 A44 Filler Percentage - % - 10 20 30 40 Tensile Strength Yield psi ASTM D638 3200 3400 2800 2550 MPa ISO 527 22 24 19 18 Tensile Elongation Yield % ASTM D638 14.0 10.0 8.0 7.0 Break % ASTM D638 >400 >400 >400 200 Flexural Modulus 73°F (23°C) psi ASTM D790 160,000 185,000 250,000 225,000 MPa ISO 178 1100 1300 1750 1550 Notched Izod 73°F (23°C) ft-lb/in ASTM D256 >10.0 >10.0 8 8.0 kJ/m2 ISO 180 55.0 55.0 44.0 14.0 Heat Deflection 66 psi °F ASTM D648 160 170 198 200 °C ISO 75 71 77 92 93 264 psi °F ASTM D648 100 105 108 112 °C ISO 75 38 41 42 44 Specific Gravity 73°F (23°C) - ASTM D792 0.96 1.04 1.15 1.25 Linear Shrinkage 1/8 in wall % - 1.2–1.6 1.0–1.4 0.8–1.2 0.6–1.0 3.2 mm wall % - 1.2–1.6 1.0–1.4 0.8–1.2 0.6–1.0 Maxxam™ Calcium Carbonate Filled Homopolymer Maxxam™ Calcium Carbonate Filled Copolymer Polypropylene Offers improved stiffness over unfilled materials as well as substantial improvement in drop weight impact and notched izod impact. Offers a high level of stiffness and heat resistance as well as excellent impact resistance Product Code - - - PP5410 B1 PP5420 B1 PP5430 B5 PP5440 B1 Reinforcement % - - - 10 20 30 40 Specific Gravity 73°F (23°C) - ASTM D792 0.96 1.05 1.14 1.23 Tensile Strength Yield psi ASTM D638 8000 10000 11500 13000 MPa ISO 527 55 69 79 90 Tensile Elongation Break % ASTM D638 8 2 2 2 Flexural Modulus 73°F (23°C) psi ASTM D790 525,000 795,000 850,000 1,000,000 MPa ISO 178 3600 5450 5800 7550 Notched Izod 73°F (23°C) ft-lb/in ASTM D256 1.10 1.30 1.50 1.60 kJ/m2 ISO 180 6.00 7.25 8.25 8.50 Heat Deflection 66 psi °F ASTM D648 280 305 310 315 °C ISO 75 138 152 154 157 264 psi °F ASTM D648 250 280 290 300 °C ISO 75 121 138 143 149 Linear Shrinkage 1/8 in wall % - 0.4–0.7 0.3–0.6 0.3–0.6 0.2–0.5 3.2 mm wall % - 0.4–0.7 0.3–0.6 0.3–0.6 0.2–0.5 Product Code - - - PP7410 A241 PP7420 B77 PP6430 A206-UV PP6435 Reinforcement % - - - 10 20 30 35 Specific Gravity Yield - ASTM D792 0.98 1.05 1.14 1.17 Tensile Strength Yield psi ASTM D638 5300 9200 9000 13300 MPa ISO 527 37 64 62 92 Tensile Elongation Break % ASTM D638 8 4 4 4 Flexural Modulus 73°F (23°C) psi ASTM D790 240,000 420,000 695,000 810,000 MPa ISO 178 1650 2900 4800 5600 Notched Izod Impact 73°F (23°C) ft-lb/in ASTM D256 5.0 1.60 1.60 2.50 kJ/m2 ISO 180 27.5 9.00 9.00 14.00 Heat Deflection 66 psi °F ASTM D648 298 313 297 300 °C ISO 75 144 156 152 149 264 psi °F ASTM D648 210 272 265 288 °C ISO 75 92 133 128 142 Linear Shrinkage 1/8 in wall % - 0.4–0.7 0.3–0.6 0.3–0.6 0.2–0.5 3.2 mm wall % - 0.4–0.7 0.3–0.6 0.3–0.6 0.2–0.5 Maxxam™ Glass Fiber Reinforced Homopolymer Polypropylene Maxxam™ Glass Fiber Reinforced Copolymer 71.866.POLYONE www.polyone.com Product Code - - - PP5312 PP5320 A285 PP5330 A123 PP5340 B2 Reinforcement % - % - 12 20 30 40 Specific Gravity 73°F (23°C) - ASTM D792 0.99 1.05 1.15 1.24 Tensile Strength Yield psi ASTM D638 4800 4400 3600 4900 MPa ISO 527 31 30 32 38 Tensile Elongation Yield % ASTM D638 5 4 4 3 Break % ASTM D638 20 15 20 10 Flexural Modulus 73°F (23°C) psi ASTM D790 285,000 380,000 355,000 460,000 MPa ISO 178 1950 2600 2450 3200 Notched Izod 73°F (23°C) ft-lb/in ASTM D256 0.6 0.55 1.5 0.60 kJ/m2 ISO 180 3.30 3.00 8.25 3.30 Heat Deflection 66 psi °F ASTM D648 235 255 230 280 °C ISO 75 113 124 110 138 264 psi °F ASTM D648 135 156 150 180 °C ISO 75 57 69 66 82 Linear Shrinkage 1/8 in wall % - 1.4–1.9 1.0–1.4 1.1–1.5 0.6–1.0 3.2 mm wall % - 1.4–1.9 1.0–1.4 1.1–1.5 0.6–1.0 Offers improved stiffness and heat deflection as well as outstanding dimensional stability.

ولكل من هذه القوانين منهج مختلف وكلها تشكل حجر الأساس في قوانين مكافحة الاحتكار في الولايات المتحدة والأساس لكثير من القوانين العالمية. 1 قانون شيرمان: الجوانب المثيرة للمخاوف المحتملة فيما يتعلق بمكافحة الاحتكار 1 الاتفاقات الأفقية. الخط الساخن للأخلاقيات في https://www.Avient.com/company/policies-and- governance/ethics-hotline فتاه 1-877-228-5410 6 mailto:ethics.officer%40avient.com?

Potensi Bidang yang Harus Diperhatikan untuk Antimonopoli 1. Saluran Langsung Etika https://www.Avient.com/company/policies-and- governance/ethics-hotline Telepon 1-877-228-5410 7 mailto:officer%40avient.com? Segera hubungi Departemen Hukum Avient dan dokumentasikan insiden tersebut. 10 Amerika Utara Kantor Pusat Global Avon Lake, Amerika Serikat 33587 Walker Road Avon Lake, OH, Amerika Serikat 44012 Nomor Bebas Pulsa: +1 866 765 9663 Nomor Telepon: +1 440 930 1000 Faks: +1 440 930 3064 Asia Pasifik Kantor Pusat Regional Shanghai, Tiongkok 2F, Block C 200 Jinsu Road Pudong, 201206 Shanghai, Tiongkok Telepon: +86 (0) 21 6028 4888 Faks: +86 (0) 21 6028 4999 Amerika Selatan Kantor Pusat Regional Sao Paulo, Brasil Av.