Common examples are polypropylene (PP), nylon (PA), polyketone (PK), and thermoplastic elastomers (TPE). Examples of semi-crystalline polymers are PP, polyethylene (PE), PA6, PA66, polyphthalamide (PPA), polybutylene/polyethylene terephthalate (PBT/PET), polyoxymethylene (POM) or acetal, polyphenylene sulfide (PPS), and polyether ether ketone (PEEK).

Nymax™ REC Recycled Nylon Formulations: two new super tough PA6 and PA66 grades added to Avient’s recycled content portfolio, each containing post-industrial recycled content, resulting in up to 81% lower cradle-to-gate product carbon footprint than traditional alternatives made without recycled content, and will be presented during Avient’s technical seminar at NPE, “Exploring Sustainable Alternatives to Traditional Polyamides,” by Jeremy Gray, Application Development and Technical Service Engineer, Specialty Engineered Materials at Avient, on May 9 at 11 a.m.

This includes Trilliant HC8910 glass-filled polyketone (PK) formulations with a lower carbon footprint than traditional nylon (PA6 and PA66) formulations for a high-performance alternative in applications such as biopharmaceutical clamps.

MATERIAL DESCRIPTION BASE RESIN Trilliant™ HC2020 Copolyester Trilliant™ HC8910/8920 Polyketone/ABS blend Trilliant™ HC2120 Tritan Trilliant™ HC3120 PC Trilliant™ HC5210 PP Trilliant™ HC6010 PA6 Trilliant™ HC6610 PA66 Trilliant™ GRV-NP-110-W PA12 TRILLIANT™ HC THERMOPLASTICS • Chemically resistant replacement for FR PC/ABS, FR PC/PET & FR COPE, providing UL 94 Yellow Card V-0 flame rating at 1.5 mm, V-1 at 0.75 mm thicknesses for a broad color spectrum • Outperforms PC/ABS, PC/PET and COPE in resistance to common disinfectants • Retains tensile strength after 72-hour exposure to common hospital disinfectants, and shows better long-term chemical resistance as compared to PC blends and COPE • Exhibits good impact and temperature resistance • Available in natural grades, standard medical colors, or custom pre-colored products • Medical device housings • MRI, X-ray, CT scanner components • Surgical instruments such as staplers, dissectors, scissors • Auto-injector pen TRILLIANT™ HC ELECTRICALLY CONDUCTIVE FORMULATIONS • Consistent conductivity ensures repeatable part performance and minimizes failures related to inconsistent electrical conductivity • High flow and easy processing facilitate filling of thin wall parts and multiple cavity tools, which enable faster cycle times and lower per-unit part costs • Superior durability reduces breakage and resultant scrap related costs • Less tendency to flash results in improved appearance and less fluid retention in or on the tip, thus driving greater accuracy and less potential for cross-contamination • High strength produces parts with greater stiffness and warp resistance, again minimizing scrap-related costs • Conductive pipette tips TEST TEMS SPECIFIC GRAVITY MELT FLOW RATE (230OC, 2.16KG) TENSILE FLEXURAL FLEXURAL MODULUS IMPACT STRENGTH NOTCHED, IZOD SURFACE RESISTIVITY Method ASTM D-792 ASTM D-1238 ASTM D-638 ASTM D-790 ASTM D-790 ASTM D-256 ASTM D-257 Unit -- g/10min MPa MPa MPa J/m Ohms/sq.

BASE RESIN PPA PC PSU PES PPS CO- POLYMER ACETAL PEEK PA Barrel Temperatures* °F (°C) Rear Zone 550–580 (288–305) 520–560 (271–293) 600–640 (316–338) 630–660 (332–338) 550–580 (288–304) 350–370 (177–188) 660–700 (349–371) 440–490 (227–254) Center Zone 560–600 (293–316) 530–570 (277–299) 620–670 (327–354) 650–680 (343–360) 560–615 (293–324) 380–390 (193–200) 700–730 (371–388) 470–510 (243–266) Front Zone 580–620 (304–327) 550–580 (288–305) 630–680 (332–360) 670–730 (354–388) 590–630 (310–332) 390–430 (200–221) 720–750 (382–400) 490–540 (254–282) Nozzle 575–615 (302–324) 550–600 (288–316) 630–680 (332–360) 680–700 (360–371) 600–625 (316–330) 380–415 (193–213) 720–750 (382–400) 520–570 (271–300) Melt Temperature 575–615 (302–324) 560–600 (293–316) 625–675 (330–358) 650–710 (343–377) 600–625 (316–330) 370–410 (188–210) 670–740 (354–393) 520–570 (271–300) Mold Temperature 250–300 (121–150) 175–240 (80–116) 190–300 (88–150) 225–325 (107–164) 250–325 (121–164) 150–225 (66–107) 290–375 (143–190) 150–200 (66–93) Pack & Hold Pressure 50%–75% of Injection Pressure Injection Velocity in/s 1.0–3.0 Back Pressure psi 50 Screw Speed rpm 50–90 Drying Parameters °F (°C) 6 hrs @ 175 (80) 4 hrs @ 250 (121) 4 hrs @ 275 (135) 4 hrs @ 300 (150) 4 hrs @ 250 (121) 2 hrs @ 200 (93) 3 hrs @ 300 (150) 4 hrs @ 180 (82) Allowable Moisture % < 0.05 < 0.02 < 0.02 < 0.04 < 0.02 0.15–0.20 < 0.02 0.10–0.20 Cushion in 0.125–0.250 Screw Compression Ratio 2.5:1–3.5:1 2.0:1–2.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 Nozzle Type General General General General General General General Reverse Taper Clamp Pressure 5–6 Tons/in2 of projected area of cavities and runner system * Barrel temperatures should be elevated for compounds designed for electrical insulative properties.

9627-GY-66 GREY ABS 9628-GY-66 GREY ABS

SHANGHAI – December 10, 2018 – PolyOne today launched a new line of super black textile colorants with outstanding darkness, superior color fastness and great spinning performance for PA and PET fibers. Compared to traditional dyes, the new super black masterbatch colorants for PA and PET fibers are a more sustainable solution.

GC-66-ULW 66

PD2/ PA HS-1 TX7 / PA HS-1 TX7 / PA GEN